富美家抗倍特板的組成及性能指數(shù)

　　Composition and performance index of Fumeijia anti double special board

　　一、抗倍特板組成圖解

　　1、 Diagram of the composition of the anti duplication special board

　　富美家抗倍特板的材質(zhì)主要是由表面透明層、裝飾色紙、褐色牛皮紙（經(jīng)過酚醛樹脂處理）層層疊壓再經(jīng)過高溫高壓制作而成的。

　　The material of Fumeijia anti double special board is mainly composed of a surface transparent layer, decorative colored paper, brown kraft paper (treated with phenolic resin) layer by layer, and then produced by high temperature and high pressure.

　　二、抗倍特板性能指標

　　2、 Performance indicators of anti duplication special board

　　目前抗倍特板（高壓熱固樹脂版）性能測試報告，國內(nèi)還沒有統(tǒng)一的產(chǎn)品標準，現(xiàn)在一般參照美國的NEMA LD-2005\ASTM D638-03\ GB/T17657-1999的方法標準來測試產(chǎn)品性能基本參數(shù)。

　　At present, there is no unified product standard in China for the performance testing report of high pressure thermosetting resin plates. Generally, the method standards of NEMA LD-2005/ASTM D638-03/GB/T17657-1999 in the United States are used to test the basic parameters of product performance.

　　材料物理性質(zhì)    標準           測試方法    樣快大小和數(shù)量    富美家測試平均值

　　Standard testing methods for physical properties of materials - Sample size and quantity - Fumeijia test average

　　拉伸強度        ASTM D638-03   采用萬能試驗機拉伸試驗      176mm*20mm*8mm5塊做成啞鈴型裝   57.3MPa

　　Tensile strength ASTM D638-03 is tested using a universal testing machine with 5 pieces of 176mm * 20mm * 8mm to make a dumbbell shaped fixture with a tensile strength of 57.3MPa

　　耐香煙灼燒性能  GB/T17657-1999 3種不同品牌的香煙放置10秒鐘  230mm*230mm*8mm  5塊     3級光澤和棕色斑都是中等程度

　　Resistance to cigarette burning performance GB/T17657-1999: Three different brands of cigarettes placed for 10 seconds, 230mm * 230mm * 8mm, 5 pieces, level 3 gloss and brown spots are moderate

　　耐干熱性    NEMA LD3-2005    恒定的溫度放置烘箱30分鐘取出后觀察  230mm*230mm*8mm5塊   表面無變化

　　Dry heat resistance NEMA LD3-2005: Place in an oven at a constant temperature for 30 minutes and observe the surface of 5 pieces with dimensions of 230mm * 230mm * 8mm without any changes

　　耐污染性     NEMA LD3-2005   用15種常用試劑取1毫升容量滴在表面放置16小時后用清洗液清洗后觀察   230mm*230mm*8mm5塊  總污染指數(shù)為1

　　Pollution resistance NEMA LD3-2005: Drop 1 milliliter of 15 commonly used reagents onto the surface and leave it for 16 hours. After cleaning with cleaning solution, observe 5 pieces of 230mm * 230mm * 8mm with a total pollution index of 1

　　抗落球沖擊性  NEMA LD3-2005   用224g的鋼球從2m處落下觀察表面如其中有一塊有變化即為有變化   230mm*230mm*8mm5塊   表面無變化

　　Impact resistance to falling balls NEMA LD3-2005: When a 224g steel ball is dropped from a distance of 2m and observed on the surface, if there is a change in one of the pieces, it is considered a change. If there is a change in 230mm * 230mm * 8mm, there is no change on the surface of the five pieces

　　表面耐磨性    NEMA LD3-2005   放置在磨耗機上用500g的力用砂紙旋轉(zhuǎn)到表面的色紙破壞取3個中的的最低值  100mm*100mm*8mm3塊  2000轉(zhuǎn)

　　Surface abrasion resistance NEMA LD3-2005. Place it on an abrasion machine and use 500g of force to rotate it with sandpaper until the colored paper on the surface is damaged. Take the lowest value of 100mm * 100mm * 8mm3 from 3 pieces and rotate them 2000 times

　　耐沸水性      NEMA LD3-2005 100度的沸水煮1個小時看變化是否分層和起鼓，如有一塊有變化即為有變化  50mm*50mm*8mm5塊    無變化

　　Boiling water resistance NEMA LD3-2005: Boil water at 100 degrees Celsius for 1 hour to see if there is any layering or bulging. If there is a change in one piece, it is a change of 50mm * 50mm * 8mm. If there is no change in five pieces, it is considered a change

　　耐刮性     NEMA LD3-2005     在刮痕儀器金剛石施以4N的力來回100次看表面變化      230mm*230mm*8mm5塊    表面無變化

　　Scratch resistance NEMA LD3-2005: Apply 4N force back and forth 100 times on the scratch instrument diamond to observe surface changes of 230mm * 230mm * 8mm. There is no change on the surface of 5 pieces

　　抗彎曲強度 GB/T17657-1999   采用萬能試驗機試驗，跨距為長度是厚度的16倍即為320mm長，50mm寬做折彎試驗  50mm*460mm*8mm5塊  158MPa

　　Bending strength GB/T17657-1999 is tested using a universal testing machine, with a span of 16 times the length and thickness, which is 320mm in length and 50mm in width. Five pieces of 158MPa are tested for bending, measuring 50mm * 460mm * 8mm

　　握螺釘力    GB/T17657-1999   用拉力儀器，拉拔板材內(nèi)的自攻螺絲，  230mm*230mm*8mm5塊    3731N

　　Gripping force of screws GB/T17657-1999: Using a tensile tester to pull self tapping screws inside the sheet metal, 5 pieces of 230mm * 230mm * 8mm 3731N

　　耐高溫性    GB/T17657-1999   放置120度攝氏度下，2小時后觀察表面  230mm*230mm*8mm5塊   表面無變化

　　High temperature resistance GB/T17657-1999: After being placed at 120 degrees Celsius for 2 hours, observe that there is no change on the surface of 5 pieces measuring 230mm * 230mm * 8mm

　　三、抗倍特板尺寸對照表

　　3、 Comparison Table of Dimensions of Anti duplication Special Plate

　　英尺       mm

　　Foot mm

　　4'*8'      1220*2440mm

　　4'*8'      1220*2440mm

　　4'*10'    1220*3050mm

　　4'*10'    1220*3050mm

　　5'*10'    1525*3050mm

　　5'*10'    1525*3050mm

　　5'*12'    1525*3660mm

　　5'*12'    1525*3660mm

　　6'*12'    1830*3660mm

　　6'*12'    1830*3660mm

　　本文由  富美家抗倍特  友情奉獻.更多有關(guān)的知識請點擊  http://m.xamgdj.com/   真誠的態(tài)度.為您提供為全面的服務.更多有關(guān)的知識我們將會陸續(xù)向大家奉獻.敬請期待.

　　This article is contributed by the friendship of Fumeijia Kangbeite For more related knowledge, please click http://m.xamgdj.com/ Sincere attitude To provide you with comprehensive services We will gradually contribute more relevant knowledge to everyone Stay tuned