由于抗倍特板材的質(zhì)地很堅硬，因此在加工時應(yīng)注意一些方面與細(xì)節(jié)點，下面富美家抗倍特廠家為您解說。

Due to the hard texture of the laminate, attention should be paid to some aspects and fine nodes during processing. Now, the manufacturer of Fumeijia Anti PET will explain it to you.

1.開料時，應(yīng)以直線鋸切為主。通?？上仍谶@種板材上畫好規(guī)格尺寸，然后再鋸切，如果工件的尺寸為標(biāo)準(zhǔn)尺寸，可先用模板劃線，再進(jìn)行鋸切，這會方便得多。

1. When cutting, it shall be mainly linear sawing. Generally, the specification and size can be drawn on this kind of plate before sawing. If the size of the workpiece is standard, the template can be used to draw a line before sawing, which will be much more convenient.

2.開孔時，可利用手提曲線鋸進(jìn)行切割，切割速度以3-4m/min為宜，如切割速度過快，一方面會使切割邊緣產(chǎn)生爆口等缺陷，另一方面也會影響鋸條的使用壽命，增加加工成本。

2. When making holes, the hand-held curve saw can be used for cutting. The cutting speed should be 3-4m/min. If the cutting speed is too fast, on the one hand, it will cause defects such as cracks at the cutting edge, on the other hand, it will also affect the service life of the saw blade and increase the processing cost.

3.加工異形邊沿時，應(yīng)先在板件表面劃出所需尺寸，然后利用曲線鋸切割；如果批量生產(chǎn)時，可利用模板進(jìn)行切割，這樣可確保加工速度和鋸切質(zhì)量。

3. When processing the irregular edge, the required size shall be marked on the surface of the plate first, and then the curve saw shall be used for cutting; In case of mass production, the template can be used for cutting to ensure the processing speed and sawing quality.

4.加工邊緣時，普遍采用的工具是手提鏤銑機(jī)，在作業(yè)前，應(yīng)清除板件表面的灰塵或異物，以免在抗倍特板件表面留下劃痕或刻痕。

4. When processing edges, the commonly used tool is a hand-held router. Before operation, the dust or foreign matters on the surface of the plate should be removed to avoid scratches or nicks on the surface of the anti magnification plate.

5.砂磨時，按順序分別采用80＃、220＃和320＃砂紙對邊緣進(jìn)行砂磨，打磨速度以15-20分鐘打磨2.5米長度為基準(zhǔn);打磨時，應(yīng)注意不要損壞表面裝飾層，打磨結(jié)束后，用拋光劑對邊緣進(jìn)行拋光處理。

5. During sanding, the edges shall be sanded with 80 ＃, 220 ＃ and 320 ＃ sandpaper in order, and the sanding speed shall be based on the length of 2.5 meters polished in 15-20 minutes; During polishing, be careful not to damage the surface decorative layer. After polishing, polish the edges with polishing agent.

6.板件拼接時，應(yīng)掌握以下幾點:a.粘合劑的涂布量應(yīng)控制在2.5-3.0g/cm2;粘接表面要全部涂布到；b.拼接后，用夾子夾緊30分鐘左右。豎直方向粘合時，一定要開口，使粘合面增大，以確保粘合強(qiáng)度；c.一旦發(fā)現(xiàn)被粘合部件有爆口等缺陷，應(yīng)將光滑平整的一面朝外，以保證粘合質(zhì)量。

6. During panel splicing, the following points shall be mastered: a. The coating amount of adhesive shall be controlled within 2.5-3.0g/cm2; The bonding surface shall be completely coated; b. After splicing, clamp for about 30 minutes. When bonding in the vertical direction, be sure to open to increase the bonding surface to ensure the bonding strength; c. Once it is found that the bonded parts have defects such as bursting, the smooth and flat side shall be outward to ensure the bonding quality.

7.如要利用螺釘連接產(chǎn)品，應(yīng)先用比螺釘直徑小的鉆頭鉆一個小孔，然后向小孔注入粘合劑，再把螺釘擰入，并保證螺釘牙紋的上沿部分?jǐn)Q入5mm以上。

7. If you want to use screws to connect products, first drill a small hole with a drill bit smaller than the screw diameter, then inject adhesive into the hole, and then screw the screw in, and ensure that the upper edge of the screw thread is screwed in more than 5mm.

8.鉆杯狀暗較鏈孔肘，板件的剩余厚度至少保留3mm以上，如剩余厚度過薄，杯狀絞鏈埋入后，會發(fā)生破損或出現(xiàn)凸痕。裝暗較鏈時，孔底和固定螺絲孔內(nèi)應(yīng)涂上粘合劑，然后再用螺釘擰緊，緊固螺釘時，不要過度，否則也會使板件邊緣部分外凸，嚴(yán)重時，會將其頂破。

8. Drill cup shaped concealed chain hole elbow, and the remaining thickness of the plate shall be at least 3 mm. If the remaining thickness is too thin, the cup shaped hinge will be damaged or convex after being embedded. When installing the concealed chain, the hole bottom and the fixing screw hole should be coated with adhesive, and then the screws should be tightened. When tightening the screws, do not excessive, otherwise the edge of the panel will also be convex, and in serious cases, it will be broken.

質(zhì)地堅硬的抗倍特怎么順利的處理？我們從以上八個操作方面了解起來，您有什么疑惑或者需求可以隨時來我們網(wǎng)站http://m.xamgdj.com進(jìn)行咨詢！

How can the hard Kangbeite be handled smoothly? We understand from the above eight operations that you can come to our website at any time if you have any doubts or needs http://m.xamgdj.com Consult!